TS-200 Rooftop King versatile waterproof paint is a single component polymer waterproof coating mainly based on acrylic latex and other polymer emulsion. After coating, a waterproof film with high elasticity, seamless, aging resistance and excellent weather resistance can be formed, which is non-toxic and environmentally friendly. It is especially suitable for roof waterproofing.
Product characteristics
It can be constructed on wet and complex base surfaces of various materials with strong film integrity.
The film has high elasticity, strong cohesion, good elongation and strong deformability.
With excellent anti-aging and water resistance, inclined roof can not be used as protective layer.
Simple construction, adjustable color, green environmental protection.
Scope of application
I It is especially suitable for waterproofing and repairing construction of metal roof.
II. Direct construction on roof, wet or dry foundation of old and new buildings.
III Sealing of expansion joints, lattice joints, falling nozzles, wall-piercing pipes, etc.
Usage method
1. Base surface treatment: Cleaning base surface, removing oil stain, moss and loose parts, must be smooth and firm; sand holes, uneven places, cracks larger than 3mm must be filled with leakage stopper king , wall corners and pipe mouth edges should be made into circular arc.
2. Repair cracks: Paint TS-200 multi-functional elastic waterproof coating twice at 10 cm on both sides of the crack. After the first surface drying (non-sticky hands), brush the second time and paste polyester non-woven cloth (cut the non-woven cloth into 6-8 cm wide strips) on the edge of the coating, and then brush it at least twice in turn according to the above method.
3. Overall brushing: first brush the corner and the edge of the pipe twice, then large area brush once after drying, and wait for the surface is dry (non-sticky hands) and then alternate brush twice or three times.
4. Too dry or too high water absorption base surface can be sprayed with a sprayer together with brushing, so that the paint fully penetrated the base surface, forming a solid three-dimensional shape of the overall waterproof layer.
Performance parameter
Reference Dosage:1.5-2.0kgs/㎡
Initial setting time: ≤4hours
Final setting time: ≤8hours
Construction temperature: +5℃~+35℃
Packaging: 5kgs/bucket, 18kgs/bucket
Implementation standard: JC/T 864-2008, specific indicators see technical parameters.
No | Project | Technical standard(II) | |
1 | Tensile strength/Mpa ≥ | 1 | |
2 | Fracture elongation /% ≥ | 300 | |
3 | Low temperature flexibility | -10℃ no crack | |
6 | Solid content /% ≥ | 65 | |
5 | Water impermeability | 0.3Mpa, 30min Impervious | |
6 | Drying time | Surface try ≤ | 4 |
Actual dry ≤ | 8 | ||
Transportation & storage
This product is non-flammable and explosive material, which can be transported according to general cargo. Sunscreen, freeze-proof, rain-proof, extrusion and collision should be avoided in transportation, and the packaging should be kept intact.
The product should be ventilated, dried and prevented from direct sunshine during storage. The storage temperature should be between 5 and 35℃.
Under normal storage and transportation conditions, the storage period is 12 months from the date of production.
Attention
After the waterproof layer is completely dry, the overburden construction can be carried out.
This material should be constructed in the environment of +5 - +35℃, and it is not suitable to be constructed outdoors in rainy weather.
This product is alkaline, if splashed into eyes will be irritating, should be washed with clear water in time.